Permanently UV-stabilized PET filament yarn

The Yarns is characterized by very good UV properties are achieved by addition of a tailor-made masterbatch during the extrusion process. The additive is physically-mechanically bonded to the polymer and is therefore inherent.

Having performed multiple exposure tests according to PV1303 (based on DIN 75202/ISO 105B06 with an irradiance of 420 nm, 1.2W/m²) results clearly show that the new UV-stabilized PET multifilament yarns, after the same exposure time, have 120% more residual strength than the standard polyester high-strength multifilament yarn without the UV stabilizer. With black-colored multifilament yarn, the residual strength increases by a further 20%.

The weathering simulation tests according to DIN/EN ISO 4892 (Artificial Irradiation or Weathering in Equipment - Xenon Arc Lamps - Methods of exposure to laboratory light sources - Xenon-arc lamps) make the differences even clearer: 60% higher residual strength compared to non UV-stabilized PET yarn.

The properties of the new functional high-performance multifilament yarns are clearly superior to the current UV-stabilized filament yarns. Strengths of 60 cN/tex at an elongation at break of 20.0% and free shrinkage values (180°C; 15min) of 1.3% are achieved, making it possible to manufacture textiles with special properties. In addition, individual customer demands can be tailor-made.

Due to the 2-stage manufacturing process, the properties such as shrinkage, specific strength/stretch are extremely constant.

Thanks to its unique molecular structure, 710UV shows significantly lower strength loss than conventional UV-stabilized polyester yarns.

In contrast to topically applied UV treatments, 710UV PET has an inherent protection that does not wash off or degrade over time.

These new PET high-strength filament yarns can be used, for example, in textile architecture, tents, silos, tarpaulins, aerospace, automotive, or outdoor/indoor sun protection.

The new yarn family will be available in titers from 76 dtex up to 6600 dtex and, if required, will also be available with S or Z twist from 60-300 twists/min.